Cobalt Chrome MoguCera Scheftner Discs

Composition in percent by mass: Co 65% Cr 28% Mo 5% C,Si,Nb,Mn,Fe <1% Technical properties: Proof stress (Rp 0.2) 413MPa Ultimate tensile strength 597MPa Elongation 12% Elastic modulus 206GPa Vickers hardness 288HV10 Density 8.3g/cm³ CTE (20-500°C) 14.5 x 10⁻⁶K⁻¹ CTE (20-600°C) 14.8 x 10⁻⁶K⁻¹ Laser weldable Yes Type (DIN EN ISO 22674) 4 Sizes: 08mm x 98.3mm with edge Ref. 138108 10mm x 98.3mm with edge Ref. 138110 12mm x 98.3mm with edge Ref. 138112 13.5mm x 98.3mm with edge Ref. 138113 15mm x 98.3mm with edge Ref. 138115 16mm x 98.3mm with edge Ref. 138116 18mm x 98.3mm with edge Ref. 138118 20mm x 98.3mm with edge Ref. 138120 25mm x 98.3mm with edge Ref. 138125 30mm x 98.3mm with edge Ref. 138130 08mm x 99.5mm without edge Ref. 138008 10mm x 99.5mm without edge Ref. 138010 12mm x 99.5mm without edge Ref. 138012 14mm x 99.5mm without edge Ref. 138013 15mm x 99.5mm without edge Ref. 138015 16mm x 99.5mm w